Fecral Heating Strip for Honeycomb Catalyst
Apr 08, 2018

Basic Info

  • Model NO.: 0Cr20Al5Y

  • Material: Fecral

  • Resisivity at 20oc: 1.4 ~1.45 Ohm Mm2/M

  • Specification: ISO9001, ISO14001

  • Product Type: Strip

  • Carbon Content: Low Carbon

  • Trademark: UALLOY

  • Origin: China

Product Description

FeCrAl heating Strip for honeycomb catalyst

1. Description
FeCrAl Alloy Strip: With the characteristics of high resistance, low coefficient of electric resistance, high
Operating temperature, good corrosion resistance under high temperature. It is mainly used in electric
Ceramic cooktop, industrial furnace.

2. Specification
1). Electric ceramic cooktop resistance strip:
Thickness: 0.04mm-1.0mm
Width: 5mm-12mm
Thickness&Width: (0.04mm-1.0mm)× 12mm(above)

2). Low resistance ribbon:
Thickness&Width: (0.2mm-1.5mm)*5mm

3). Industrial furnace ribbon:
Thickness: 1.5mm-3.0mm
Width: 10mm-30mm
4). Wire: Diameter: 0.05mm-10.0mm


3. Usage
It is mainly used in electric locomotive, diesel locomotive, metro vehicle and high speed moving ca, catalytic converter, brake system brake resistor, electric ceramic cooktop, industrial furnace etc.

4. Features
Stable performance; Anti-oxidation; Corrosion resistance; High temperature stability; Excellent coil-forming ability; Uniform and beautiful surface condition without spots.

5. Packing detail
1) Coil (plastic spool) + compressed ply-wooden case + pallet
2) Coil (plastic spool) + carton + pallet

6. Products and services
1). Pass: ISO9001 certification, and SO14001cetification;
2). Fine after-sale services;
3). Small order accepted;
4). Stable properties in high temperature;
5). Fast delivery;

CPSReSiCrYAlFeZrTiCa+Mn
Max0.04Max 0.02Max 0.0150.3Max 0.420Max 0.15Bal.0.20.150.5

 
Mechanical Properties

Max Continuous Service Temp1300ºC
Resisivity at 20ºC1.4 ~1.45 ohm mm2/m
Density7.10 g/cm3
Thermal Conductivity46.1KJ/m@h@ºC
Coefficient of Thermal Expansion16.0×10-6/ºC
Melting Point1500ºC
Tensile Strength637~784 Mpa
ElongationMin 12%
Section Variation Shrink Rate65~75%
Repeatedly Bend FrequencyMin 5 times
Continuous Service Time-
Hardness200-260HB
Micrographic StructureFerrite
Magnetic PropertyMagnetic